Forum Discussion

speranskyanton's avatar
speranskyanton
Icon for Occasional Contributor rankOccasional Contributor
1 year ago

5M2210ZF256I5N

Hello! I really need your help with part number 5M2210ZF256I5N. What solder ball alloy composition is acceptable if the original documentation specifies Sn 96.5%, Ag 3%, Cu 0.5%? How can we determ...
Fpga Devkit
NurAiman_M_Intel's avatar
NurAiman_M_Intel
Icon for Super Contributor rankSuper Contributor
11 months ago

Hi,


Update from our quality team,


Below are the existing criteria.

While some of these units may fail the criteria, specifically the scratches, we have not had any history of validated failures associated with surface scratches such as what is seen on these images.

Substrate scratches:

  • Reject scratch greater than 80 mils (~2mm) in any direction.

Solder ball criteria:

  • Visible damage at 1x magnification (naked eye or unaided human vision inspection) that leads to out of spec ball height.
  • Reject if any foreign material is found on solder balls with length greater than half the ball diameter.
  • Reject for any visible misalignment (against the pad) at 1x magnification (naked eye or unaided human vision inspection).

Regards,

Aiman


  • speranskyanton's avatar
    speranskyanton
    Icon for Occasional Contributor rankOccasional Contributor
    11 months ago

    Hello,
    Thank you very much for the quick and thorough response.
    Just to confirm — would you say that the photos with the defects I sent you look acceptable in the end?
    Thank you!

Recent Discussions